Halfway through the twentieth century, the steelmaking process was transformed when the batch process of ingot casting was replaced by continuous casting. With this technique, a constant stream of liquid steel is transformed into endless strands of glowing, solid metal (see Figures 1 and 2).
Figure 2. Continuous casting diagram. Liquid steel is brought to the caster in ladles. The tundish distributes the liquid steel to the copper moulds and the formed strands are withdrawn out of the moulds using driven rollers.
In ingot casting, the head of each ingot must be cropped after it is removed from the mould, producing waste metal. In continuous casting, however, this cropping must only be done at the very start and very end of each sequence during which several hundred tons of steel are cast, meaning far less waste material is produced. Additionally, the shape of the cast strands is far closer to the shape of the final rolled product. This results in improved yield, superior quality, and better cost efficiency than previous methods. Not surprisingly, 95% of steel is made using continuous casting today.
SMS Concast has been a leader in this field for 60 years, designing and building technical equipment for steel melting, refining, and continuous casting. It has a worldwide market share of over 40%. “Continuous casting presents a huge number of variables that we need to analyse as we continue to improve the technology and advance the boundaries of what we know,” explains Nicholas Grundy, head of Metallurgy & Process Continuous Casting at SMS Concast. “We are constantly pushing the limits and the only way to understand something that we have never done before is to simulate it.”
Simulation Across All Realms
In continuous casting, molten, refined steel is typically brought to the caster in ladles of 30 to 350-ton capacity. The steel is teemed into a tundish that distributes the steel into one to eight strands. The first solid steel is formed in the open-ended, water-cooled copper moulds and the formed strands are withdrawn out of the moulds using driven rollers at speeds of 0.1 to 6m per minute, depending on section size (see Figure 2). After fully solidifying, the red-hot strands are cut into 3 to 15m-long pieces and left to cool.
The process of continuous casting produces a cast semifinished that is close in shape to the final product, greatly reducing the cost of further processing by rolling or forging. Depending on the shape of the mould, square profiles called billets can be cast for rolling into bars and wire for applications ranging from concrete reinforcement to piano wire. Larger, rectangular pieces called blooms can also be forged, for example to form a crankshaft or to be rolled into bars or rails. Slabs are rolled into sheet metal out of which everything from cars to oil tankers are produced.
SMS Concast uses simulation at every stage of the casting process: To analyse fluid flow in the tundish, primary solidification in the mould, solidification and mechanical deformation of the strand, and quenching or slow cooling of the cut blooms. “During solidification, we must minimize segregation of alloying elements towards the centre of the strand, remove non-metallic inclusions, and improve the microstructure of the solidifying steel,” described Grundy.
“One way of achieving these improvements is by stirring the liquid steel,” he said (see Figure 3). This is done using electromagnetic stirrers that generate strong rotating electromagnetic fields around the strands. This causes the liquid steel in the core of the strands to rotate. The field generated by the stirrers and the resulting flow pattern of the liquid steel is simulated using COMSOL Multiphysics. Simulation is a crucial step in order to design the electromagnetic stirrers correctly and to achieve the best steel quality. Stirring is particularly important for highly-alloyed grades such as ball bearing steel, with high demands on cleanliness (with a minimal presence of non-metals), even composition (low segregation), and fine-grained microstructure.
Figure 3. Model of a tundish using the CFD Module in COMSOL Multiphysics (top) and actual tundish during emptying of molten steel (bottom).
“Essentially, most of the problems we face must be studied by combining various realms of physics such as electromagnetics, liquid or gas flow, mechanics and heat transfer. That’s why we use COMSOL Multiphysics; we know of no other tool that links all these realms of physics into one single platform as seamlessly as COMSOL.”
Predicting solidification and shrinkage
One recent steelmaking trend is to roll strands of cast steel while they are still hot, rather than cooling them down and reheating them later in a reheating furnace. This is called hot charging, and avoids wasteful loss of thermal energy but demands an even more accurate understanding of how a strand solidifies. Grundy explained, “The copper mould is at the heart of each continuous caster. This is where the first solid steel skin is formed. A billet will only be faultless if the internal shape of the copper tube follows the shrinkage of the steel exactly, and a billet’s surface must be faultless if it’s to be hot-charged.”
The SMS Concast team used their COMSOL model to understand the complex heat exchange processes taking place during the first solidification of the steel in the mould. The results guided the design of a new type of mould to cast billets with large rounded corners (see Figure 4). These corners stay warm after casting, resulting in a more even surface temperature. This makes it possible to hot-charge the billets directly to the rolling mill, without leaving them to cool down and then heating them again in a reheating furnace fired with fossil fuels, as is the practice in a conventional steel plant.
Figure 4. The water-cooled copper mould tube where the first solid steel shell forms is the heart of every continuous caster (top). Model of primary solidification and shell growth in the copper mould (bottom).
The innovative mould design was successfully implemented at Tung Ho Steel in Taiwan in 2010, a steel plant that runs completely without a gas-fired reheating furnace, resulting in huge environmental and economic benefits. This reduces yearly emissions by 40,000 tons of CO2, about the same as the exhaust of 20,000 cars.
Simulate but also validate
Grundy concluded, “Whenever possible, we like to validate our simulations with results from the real world or with physical models. For example, to validate our tundish flow simulation, one customer built a Plexiglas scaled water model and we found excellent agreement between the physical model and our flow simulations. As trust in our models grows, we gain the confidence to explore allowable designs.” This approach clearly works well for the company; the world’s widest beam blank (1150 x 490 x 130mm) is already being cast on an SMS Concast caster in Germany, and the largest round section ever made (1000mm in diameter) will go into production in a South Korean mill in 2015.
Nicholas Grundy displaying the simulation results of one of the CFD models of the continuous casting process.